Categories
- New arrivals
- Products on sale
- Steel for knifemaking [149]
- Carbon steel - tool steel [65]
- Stainless knifemaking steel [78]
- 1.4116 (X50CrMoV15) steel for knifemaking [22]
- CPM stainless knife steel [2]
- DAMASTEEL® Thor™ [0]
- N360 Böhler 1.4108 acél [2]
- N690 Böhler 1.4528 [10]
- N695-1.4125-440c [2]
- M390 Böhler [12]
- 12C27 Sandvik knifemaking steel [5]
- 14C28N Sandvik stainless knifemaking steel [3]
- AEB-L Uddeholm steel [6]
- SF100 [1]
- RWL34 Steel [3]
- Nitrobe77 [1]
- BECUT [1]
- VG10 San-Mai Laminated steel [4]
- ELMAX Uddeholm knife steel [2]
- 440B - 1.4112 - stainless steel [1]
- Nitrocut NCV60/AISI 304 Sandwich [1]
- Damasc steel - ONLY TO ORDER [6]
- Knife handle materials [228]
- Surface treatment tools [32]
- Screws [27]
- Mosaic pins [29]
- Bolsters [41]
- Tubes and pins [44]
- Brass square bar, closed section, angle profile [16]
- steel folie [1]
- Luiso W61 Antioxidant Protective Paste Liquid [2]
- Blades and knife blanks [80]
- Kitchen knives [5]
- Knife sheath materials [49]
- Knife and folding knife kits [8]
- Tools for knifemaking [22]
- Drill bits [29]
- Circular saw blades [4]
- Lamellar sanding disc 125mm x 22mm [8]
- Abrasive belts 50x1200mm [25]
- Abrasive belts 50x1500mm [17]
- Abrasive belts 50x2000mm [52]
- 50x2500mm csiszolószalag [1]
- Adhesives [1]
- Sharpening [4]
Vote
Recommended products
Visitor counter
0
4
0
7
5
6
9
Partners
Certificate
Product Details
| Stock |
2 pcs
|
| Weight |
1 kg/pcs
|
| Short description | Böhler N360, also known as 1.4108 or X30
BÖHLER N360 is a highly corrosion-resistant, martensitic steel. Compared to conventional CrMo steels, it has significantly improved corrosion and toughness properties with high hardness.
C: 0.3 Si: 0.6 Mn: 0.4 Cr: 15.0 Mo: 1.0 N: 0.4
-heated / cross-rolled -softened -relaxed
Heat treatment variant I (including deep-freezing): Available final hardness: 59 - 60 HRC - Training at 1030 ° C in oil (holding time: 30 minutes) - Freeze at -80 ° C for one hour - tempering at 150 ° C (2x 2 hours) Heat treatment version (without freezing): Available final hardness: approx. 58 HRC - Training at 1030 ° C in oil (holding time: 30 minutes) - tempering at 200 ° C (2x 2 hours) |